Alusil

EN Texte en anglais Pas encore d'article dans ta langue : extrait en anglais.

Alusil as a hypereutectic aluminium-silicon alloy (EN AC-AlSi17Cu4Mg / EN AC-48100 or A390) contains approximately 78% aluminium and 17% silicon. This alloy was theoretically conceived in 1927 by Schweizer & Fehrenbach, of Badener Metall-Waren-Fabrik, but practically created only by Lancia in the same year, for its car engines. It was further developed by Reynolds, now Rheinmetall Automotive. In the United States, Chevrolet was the first to use Reynolds A390 in the Chevrolet Vega. The Alusil aluminium alloy is commonly used to make linerless aluminium alloy engine blocks. There is no coating applied to the cylinder bore and blocks are not honed conventionally. During the manufacturing process, a chemical or mechanical process is used to remove aluminium from the surface of the cylinder bore, exposing a very hard silicon precipitate. These exposed silicon particles, which under a microscope look like small islands, allow for oil to collect in the area surrounding them, thus forming the required tribofilm that supports piston and ring travel. The pistons used in an Alusil engine block typically have an iron-clad plating or similar coating on the piston skirts to prevent galling of the aluminium pistons when run against the uncoated aluminium cylinder bore. Examples of this coating include Mahle Ferrostan (I & II), FerroTec, or Ferroprint. BMW switched from Nikasil-coated cylinder walls to Alusil in 1996 to eliminate the corrosion problems caused through the use of petrol/gasoline containing sulfur. Although similar, Alusil is not to be mistaken with Lokasil which was used by Porsche in the Boxster, Cayman, and 911 models from 1997 through 2008. Lokasil blocks use a freeze-cast cylinder sleeve pre-form which is inserted into the casting mold. This preform contains silicon particles suspended in a resin binder. During the casting process, the molten aluminium is injected into the mold and burns off the...